PU Electrostatic Paint Primer-White

PU Electrostatic Paint Primer-White

It is a primer with electrically charged paint particles designed to be used in plants with manual and robotic wet paint application. In generally, it is suitable for negative (-) charging of liquid paints during spraying and for priming the conductive surface to be painted by grounding. It has high filling and hiding power. It can be sanded easily and creates a smooth surface for cellulosic, polyurethane-based topcoat paints to be applied. It provides transfer efficiency up to 90%.

Product Features

Geri
İleri
  • Product Name
  • Product Description
  • Chemical Structure
  • TDS
  • SDS
  • Density, 20°C gr/cm3
  • Viscosity, 25°C, KU
  • Solid (by weight) ,%
  • Set-to-Touch Time, min.
  • Tack-free Time, min.
  • Sanding Time, hour
  • Product Highlights
  • Areas of usage
  • Mixing Ratio
  • Recommended Use
  • Storage Conditions
  • Package Type
  • explanation
  • PA.911
  • Polyurethane Electrostatic White Primer
  • Polyurethane
  • 1,545± 0,03
  • 115± 5
  • 75± 3
  • 10± 5
  • 40± 5
  • 12± 2
  • *Enabling more material to be painted with less primer with the electrostatic "wrapping" effect *Easy to sand
    *High covering and filling power *Crack resistant *Ensuring transfer efficiency *Reducing paint-thinner consumption
  • It is used in furniture and decoration works to provide the smooth surface required for top coat varnish application on all kinds of wooden surfaces (chipboard, mdf, wood veneer and solid surfaces).
  • PA.911 : 100
    SP.160 : 50
    PLT-4011 : 5-10
  • The surface must be clean and dry, free of dirt and dust. Before use, the filler varnish should be mixed thoroughly and homogenized. After mixing with the thinner and hardener properly, it is applied on the surface with a pistol. If the ambient temperature is 23°C according to the desired fullness, it is waited for 15-20 minutes between the layers and 2-3 layers of cross application can be made in the form of 90+100+100 gr/m2. During the application, the ambient temperature should not be below 5 °C. It is recommended to sand after waiting for 6 hours in summer and 24 hours in winter.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.