Acrylic High-Gloss Varnish

Acrylic High-Gloss Varnish

It gives high gloss and full appearance to the applied surface. No loss of gloss over time. It does not require much time for the paste-polishing process. It can be applied on special effect paints. It is not prone to boiling.

Product Features

  • Product Name
  • Product Description
  • Chemical Structure
  • TDS
  • SDS
  • Density, 20°C gr/cm3
  • Viscosity, 25°C, DIN4 sec.
  • Solid (by weight) ,%
  • Gloss, gloss 60º
  • Set-to-Touch Time, min.
  • Tack-free Time, min.
  • Dry-hard time, hour
  • Dry-Through time, day
  • Product Highlights
  • Areas of usage
  • Mixing Ratio
  • Recommended Use
  • Storage Conditions
  • Package Type
  • explanation
  • AV00.440
  • Acrylic High-gloss Varnish
  • Acrylic
  • 0,98± 0,03
  • 20± 5
  • 48± 3
  • 95± 3
  • 40± 5
  • 70± 10
  • 48± 5
  • 3± 1
  • *High gloss before and after polishing
    *Good spread and and plump appearance after application
    *Maximum resistance to yellowing
  • It is applied as a top coat varnish on all kinds of MDF, solid and coated wooden surfaces, polyurethane, polyester filler varnish or lacquer polyester prepared in advance, with furniture decoration works.
  • AV00.440 : 100
    SA.1020 : 50
    PLT-4000/ AT-100 : 15-20
  • Surface must be clean and dry, free of dirt and dust.
    Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
    It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 2-3 layers of 100-100-130 gr/m3 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 15 kg /3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • AV00.450
  • Acrylic High-gloss Varnish
  • Acrylic
  • 0,98± 0,03
  • 20± 5
  • 45± 3
  • 95± 3
  • 25± 5
  • 55± 10
  • 40± 5
  • 3± 1
  • *High gloss before and after polishing
    *Good spread and and plump appearance after application
    Maximum resistance to yellowing *Fast drying
  • It is applied as a top coat varnish on all kinds of MDF, solid and coated wooden surfaces, polyurethane, polyester filler varnish or lacquer polyester prepared in advance, with furniture decoration works.
  • AV00.450 : 100
    SA.1020 : 50
    PLT-4000/ AT-100 : 15-20
  • Surface must be clean and dry, free of dirt and dust.
    Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
    It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 2-3 layers of 100-100-130 gr/m3 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 15 kg /3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.