PU Electrostatic High-Gloss Paint

It is a paint with electrically charged paint particles designed to be used in plants where manual and robotic wet paint is applied. In generally, it is suitable for negative (-) charging of liquid paints during spraying and for priming the conductive surface to be painted by grounding. It has high gloss and hiding power.

Product Features

Product Name
Product Description
Chemical Structure
TDS
SDS
Density, 20°C gr/cm3
Viscosity, 25°C, DIN4 sec.
Solid (by weight) ,%
Gloss, gloss 60º
Set-to-Touch Time, min.
Tack-free Time, min.
Dry-hard time, hour
Dry-Through time, day
Product Highlights
Areas of usage
Mixing Ratio
Recommended Use
Storage Conditions
Package Type
explanation

PB00.811
Polyurethane Electrostatic High-Gloss White Paint
Polyurethane
1,200± 0,03
75± 5
62± 3
98± 3
25± 5
75± 15
24± 5
3± 1
*Ensuring the varnishing of more materials with less filling varnish with the electrostatic "wrapping" effect *High opacity
*Good spreading and fuller appearance after application
*High yellowing resistance
It is applied as a top coat paint on all kinds of MDF, solid and veneered wooden surfaces, polyurethane or polyester primer prepared in advance, with furniture decoration works.
PB00.811 : 100
SP.170 : 50
PLT-4011 : 20-25
Surface must be clean and dry, free of dirt and dust.
Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 3 layers of 90+110+110 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
12 kg
*The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.