Polyurethane High-Gloss Varnishes

Polyurethane High-Gloss Varnishes

It provides the desired high-gloss and slipperiness to the applied surface. It is a top coat varnish with a glossy appearance that physically; hard, resistant to scratches and impacts, chemically; resistant to water, detergent and other chemical factors. It has vibrant and high transparency.

Product Features

  • Product Name
  • Product Description
  • Chemical Structure
  • TDS
  • SDS
  • Density, 20°C gr/cm3
  • Viscosity, 25°C, DIN4 sec.
  • Solid (by weight) ,%
  • Gloss, gloss 60º
  • Set-to-Touch Time, min.
  • Tack-free Time, min.
  • Dry-hard time, hour
  • Dry-Through time, day
  • Product Highlights
  • Areas of usage
  • Mixing Ratio
  • Recommended Use
  • Storage Conditions
  • Package Type
  • explanation
  • PAV00.412
  • Polyacrylic High-gloss Varnish-Yellowing Resistance
  • Polyacrylic
  • 0,99± 0,03
  • 17± 5
  • 50± 3
  • 98± 3
  • 75± 15
  • 40± 5
  • 24± 5
  • 2± 1
  • *High gloss before and after polishing
    *Good spread and and plump appearance after application
    *Maximum yellowing resistance *Fast drying (can be polished after 24 hours)
  • It is applied as a top coat varnish on all kinds of MDF, solid and coated wooden surfaces, polyurethane, polyester filler varnish or lacquer polyester prepared in advance, with furniture decoration works.
  • PAV00.412 : 100
    SP.250 : 100
    PLT-4000/SLT-2000 : 5-10
  • Surface must be clean and dry, free of dirt and dust.
    Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
    It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 2-3 layers of 90+120+120 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg /2,8 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • PV00.410
  • Polyurethane High-gloss Varnish
  • Polyurethane
  • 1,025± 0,03
  • 50± 5
  • 55± 3
  • 100± 3
  • 75± 15
  • 40± 5
  • 24± 5
  • 3± 1
  • *High gloss before and after polishing
    *Good spread and and plump appearance after application
    *Fast drying
  • It is applied as a top coat varnish on all kinds of MDF, solid and coated wooden surfaces, polyurethane, polyester filler varnish or lacquer polyester prepared in advance, with furniture decoration works.
  • PV00.410 : 100
    SP.100 : 100
    PLT-4000/SLT-2000 : 5-10
  • Surface must be clean and dry, free of dirt and dust.
    Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
    It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 30-60 minutes, 2-3 layers of 90+120+120 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg /3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • PV00.421
  • Polyurethane Superlux High-gloss Varnish
  • Polyurethane
  • 1,02± 0,03
  • 60± 5
  • 55± 3
  • 100± 3
  • 75± 15
  • 40± 5
  • 24± 5
  • 3± 1
  • *High gloss before and after polishing
    *Good spread and and plump appearance after application
    *Fast drying
  • It is applied as a top coat varnish on all kinds of MDF, solid and coated wooden surfaces, polyurethane, polyester filler varnish or lacquer polyester prepared in advance, with furniture decoration works.
  • PV00.421 : 100
    SP.190 : 100
    PLT-4000/SLT-2000 : 5-10
  • Surface must be clean and dry, free of dirt and dust.
    Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
    It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 2-3 layers of 90+120+120 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg /3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • PV00.422
  • Polyurethane Superlux High-Gloss Varnish
  • Polyurethane
  • 1,02± 0,03
  • 60± 5
  • 55± 3
  • 100± 3
  • 75± 15
  • 40± 5
  • 24± 5
  • 3± 1
  • *High gloss before and after polishing
    *Good spread and and plump appearance after application
    *Fast drying
  • It is applied as a top coat varnish on all kinds of MDF, solid and coated wooden surfaces, polyurethane, polyester filler varnish or lacquer polyester prepared in advance, with furniture decoration works.
  • PV00.422 : 100
    SP.100 : 50
    PLT-4000/SLT-2000 : 5-10
  • Surface must be clean and dry, free of dirt and dust.
    Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
    It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 2-3 layers of 90+120+120 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg /3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • PV00.431
  • Polyurethane High-gloss Varnish
  • Polyurethane
  • 0,985± 0,03
  • 60± 5
  • 45± 3
  • 100± 3
  • 75± 15
  • 40± 5
  • 24± 5
  • 3± 1
  • *High gloss before and after polishing
    *Good spread and and plump appearance after application
    *Fast drying
  • It is applied as a top coat varnish on all kinds of MDF, solid and coated wooden surfaces, polyurethane, polyester filler varnish or lacquer polyester prepared in advance, with furniture decoration works.
  • PV00.431 : 100
    SP.150 : 100
    PLT-4000/SLT-2000 : 5-10
  • Surface must be clean and dry, free of dirt and dust.
    Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
    It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 2-3 layers of 90+120+120 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg /3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • PV00.432
  • Polyurethane High-gloss Varnish
  • Polyurethane
  • 0,985± 0,03
  • 60± 5
  • 45± 3
  • 100± 3
  • 75± 15
  • 40± 5
  • 24± 5
  • 3± 1
  • *High gloss before and after polishing
    *Good spread and and plump appearance after application
    *Fast drying
  • It is applied as a top coat varnish on all kinds of MDF, solid and coated wooden surfaces, polyurethane, polyester filler varnish or lacquer polyester prepared in advance, with furniture decoration works.
  • PV00.432 : 100
    SP.110 : 50
    PLT-4000/SLT-2000 : 5-10
  • Surface must be clean and dry, free of dirt and dust.
    Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
    It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 2-3 layers of 90+120+120 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg /3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.