Polyurethane Converter Paints - 1. Group

Polyurethane Converter Paints - 1. Group

It is a two-component paint bases designed for coloring system. It is used in the preparation of polyurethane-based glossy, silk matte and matte colors in the Color System. It has a mixing ratio of 4/1. Compatible with universal pastes.

Product Features

  • Product Name
  • Product Description
  • Chemical Structure
  • TDS
  • SDS
  • Density, 20°C gr/cm3
  • Viscosity, 25°C, DIN4 sec.
  • Solid (by weight) ,%
  • Areas of usage
  • Recommended Use
  • Storage Conditions
  • Package Type
  • explanation
  • BBP00.800.0000
  • Tinting PU High-Gloss Transparent Converter Paint
  • Polyurethane
  • 1,020± 0,03
  • 85± 5
  • 55± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,20 kg / 2,55 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP50.800.0000
  • Tinting PU Silky Matt Transparent Converter Paint
  • Polyurethane
  • 1,200± 0,03
  • 85± 5
  • 65± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,20 kg / 2,55 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP25.800.0000
  • Tinting PU Matt Transparent Converter Paint
  • Polyurethane
  • 1,200± 0,03
  • 85± 5
  • 65± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,20 kg / 2,55 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP10.800.0000
  • Tinting PU Matt Transparent Converter Paint
  • Polyurethane
  • 1,200± 0,03
  • 85± 5
  • 65± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,20 kg / 2,55 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP00.800.1000
  • Tinting PU High-Gloss White Base
  • Polyurethane
  • 1,200± 0,03
  • 85± 5
  • 65± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg / 3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP50.800.1000
  • Tinting PU Silky Matt White Converter Paint
  • Polyurethane
  • 1,350± 0,03
  • 85± 5
  • 70± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg / 3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP25.800.1000
  • Tinting PU Matt White Converter Paint
  • Polyurethane
  • 1,350± 0,03
  • 85± 5
  • 70± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg / 3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP10.800.1000
  • Tinting PU Matt White Converter Paint
  • Polyurethane
  • 1,350± 0,03
  • 85± 5
  • 70± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg / 3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP00.800.1100
  • Tinting PU High-Gloss Semi White Converter Paint
  • Polyurethane
  • 1,100± 0,03
  • 85± 5
  • 58± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,80 kg / 2,70 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP50.800.1100
  • Tinting PU Silky Matt Semi White Converter Paint
  • Polyurethane
  • 1,300± 0,03
  • 85± 5
  • 68± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,80 kg / 2,70 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP25.800.1100
  • Tinting PU Matt Semi White Converter Paint
  • Polyurethane
  • 1,300± 0,03
  • 85± 5
  • 68± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,80 kg / 2,70 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP10.800.1100
  • Tinting PU Matt Semi White Converter Paint
  • Polyurethane
  • 1,300± 0,03
  • 85± 5
  • 68± 3
  • In Tinting systems, PU based RAL, NCS, Pantone etc. These are base types used in the preparation of color charts and all desired colors. It is used in cases where yellowing is not desired.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.195 at a ratio of 2/1 for matte systems, and thoroughly mixed with SP.170 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a gun to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,80 kg / 2,70 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.