Polyurethane Converter Paints - 2. Group

Polyurethane Converter Paints - 2. Group

Two-component paint bases designed for coloring system. It is used in the preparation of polyurethane-based glossy, silk matte and matte colors in the Color System. It has a mixing ratio of 2/1. It is recommended to use Eskim SP.195 hardeners for matte paints and Eskim SP.170 hardeners for glossy paints. Compatible with universal pastes.

Product Features

  • Product Name
  • Product Description
  • Chemical Structure
  • TDS
  • SDS
  • Density, 20°C gr/cm3
  • Viscosity, 25°C, DIN4 sec.
  • Solid (by weight) ,%
  • Areas of usage
  • Recommended Use
  • Storage Conditions
  • Package Type
  • explanation
  • BBP50.850.1000
  • Tinting PU Silk Matt White Converter Paint
  • Polyurethane
  • 1,36± 0,03
  • 85± 5
  • 66± 3
  • They are base types used in the preparation of all desired colors with PU-based RAL, NCS, Pantone etc. color charts in coloring systems.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.185 at a ratio of 4/1 for matte systems, and mixed thoroughly with 2/1 SP.100 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a spray machine to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg / 3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP25.850.1000
  • Tinting PU Matt White Converter Paint
  • Polyurethane
  • 1,36± 0,03
  • 85± 5
  • 66± 3
  • They are base types used in the preparation of all desired colors with PU-based RAL, NCS, Pantone etc. color charts in coloring systems.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.185 at a ratio of 4/1 for matte systems, and mixed thoroughly with 2/1 SP.100 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a spray machine to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg / 3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP10.850.1000
  • Tinting PU Matt White Converter Paint
  • Polyurethane
  • 1,36± 0,03
  • 85± 5
  • 66± 3
  • They are base types used in the preparation of all desired colors with PU-based RAL, NCS, Pantone etc. color charts in coloring systems.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.185 at a ratio of 4/1 for matte systems, and mixed thoroughly with 2/1 SP.100 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a spray machine to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 12 kg / 3 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP50.850.0000
  • Tinting PU Silky Matt Transparent Converter Paint
  • Polyurethane
  • 85± 5
  • 63± 3
  • They are base types used in the preparation of all desired colors with PU-based RAL, NCS, Pantone etc. color charts in coloring systems.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.185 at a ratio of 4/1 for matte systems, and mixed thoroughly with 2/1 SP.100 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a spray machine to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,20 kg / 2,55 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP25.850.0000
  • Tinting PU Matt Transparent Converter Paint
  • Polyurethane
  • 85± 5
  • 63± 3
  • They are base types used in the preparation of all desired colors with PU-based RAL, NCS, Pantone etc. color charts in coloring systems.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.185 at a ratio of 4/1 for matte systems, and mixed thoroughly with 2/1 SP.100 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a spray machine to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,20 kg / 2,55 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP10.850.0000
  • Tinting PU Matt Transparent Converter Paint
  • Polyurethane
  • 85± 5
  • 63± 3
  • They are base types used in the preparation of all desired colors with PU-based RAL, NCS, Pantone etc. color charts in coloring systems.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.185 at a ratio of 4/1 for matte systems, and mixed thoroughly with 2/1 SP.100 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a spray machine to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,20 kg / 2,55 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP50.850.1100
  • Tinting PU Silky Matt White Converter Paint
  • Polyurethane
  • 1,30± 0,03
  • 85± 5
  • 65± 3
  • They are base types used in the preparation of all desired colors with PU-based RAL, NCS, Pantone etc. color charts in coloring systems.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.185 at a ratio of 4/1 for matte systems, and mixed thoroughly with 2/1 SP.100 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a spray machine to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,80 kg / 2,70 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP25.850.1100
  • Tinting PU Matt White Converter Paint
  • Polyurethane
  • 1,30± 0,03
  • 85± 5
  • 65± 3
  • They are base types used in the preparation of all desired colors with PU-based RAL, NCS, Pantone etc. color charts in coloring systems.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.185 at a ratio of 4/1 for matte systems, and mixed thoroughly with 2/1 SP.100 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a spray machine to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,80 kg / 2,70 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.
  • BBP10.850.1100
  • Tinting PU Matt White Converter Paint
  • Polyurethane
  • 1,30± 0,03
  • 85± 5
  • 65± 3
  • They are base types used in the preparation of all desired colors with PU-based RAL, NCS, Pantone etc. color charts in coloring systems.
  • The color desired to be prepared in the Tinting System is selected from the color chart and combined with the appropriate matte base and the amount of paste in the color formula. It is mixed until the color becomes completely homogeneous. The color prepared in this way is mixed with SP.185 at a ratio of 4/1 for matte systems, and mixed thoroughly with 2/1 SP.100 for glossy systems. It is thinned to the application viscosity with Polyurethane Thinner/Cellulosic Thinner and applied with a spray machine to the previously primed surface. Wait for min. 30 minutes between coats.
  • It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
  • 10,80 kg / 2,70 kg
  • *The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.