Polyurethane Glossy Paints

The top coat white furniture paints. It has high physical and chemical resistance, easy to apply and gives a glossy and slippery appearance to the applied surface. It is resistant to scratch and impact. It has a high hiding power. It has a high gloss before and after polishing.

Product Features

Product Name
Product Description
Chemical Structure
TDS
SDS
Density, 20°C gr/cm3
Viscosity, 25°C, DIN4 sec.
Solid (by weight) ,%
Gloss, gloss 60º
Set-to-Touch Time, min.
Tack-free Time, min.
Dry-hard time, hour
Dry-Through time, day
Product Highlights
Areas of usage
Mixing Ratio
Recommended Use
Storage Conditions
Package Type
explanation

PB00.1000
Polyurethane High-Gloss White Paint-High Yellowing Resistant
Polyurethane
1,36± 0,03
70± 5
70± 3
98± 3
25± 5
75± 15
24± 5
3± 1
*High gloss before and after polishing *Excellent spread and plump appearance after application
*Maximum resistance to yellowing
*Fast drying
*Higher hiding power
It is applied as a top coat paint on all kinds of MDF, solid and veneered wooden surfaces, polyurethane or polyester primer prepared in advance, with furniture decoration works.
PB00.1000 : 100
SP.215 : 100
PLT-4000/SLT-2000 : 10-15
Surface must be clean and dry, free of dirt and dust.
Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 3 layers of 90+110+110 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
12 kg /3 kg
*The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.

PB00.812
Polyurethane High-Gloss White Paint-High Yellowing Resistant
Polyurethane
1,30± 0,03
75± 5
67± 3
95± 3
25± 5
75± 15
24± 5
3± 1
*Excellent spread and plump appearance after application
*Maximum resistance to yellowing
*Higher hiding power *High gloss before and after polishing
It is applied as a top coat paint on all kinds of MDF, solid and veneered wooden surfaces, polyurethane or polyester primer prepared in advance, with furniture decoration works.
PB00.812 : 100
SP.205 : 50
PLT-4000/SLT-2000 : 20-25
Surface must be clean and dry, free of dirt and dust.
Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 3 layers of 80-110-110 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
12 kg /3 kg
*The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.

PB00.810
Polyurethane High-Gloss White Paint-Yellowing Resistant
Polyurethane
1,30± 0,03
85± 5
67± 3
95± 3
25± 5
75± 15
24± 5
3± 1
*Excellent spread and plump appearance after application
*Resistance to yellowing
*Higher hiding power *Fast drying
It is applied as a top coat paint on all kinds of MDF, solid and veneered wooden surfaces, polyurethane or polyester primer prepared in advance, with furniture decoration works.
PB00.810 : 100
SP.170 : 50
PLT-4000/SLT-2000 : 20-25
Surface must be clean and dry, free of dirt and dust.
Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 3 layers of 80-110-110 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
12 kg /3 kg
*The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.

PB00.812.99
Polyurethane High-Gloss Black Paint
Polyurethane
1,36± 0,03
70± 5
70± 3
98± 3
25± 5
75± 15
24± 5
3± 1
*Excellent spread and plump appearance after application
*High gloss before and after polishing *Deep blackness
It is applied as a top coat paint on all kinds of MDF, solid and veneered wooden surfaces, polyurethane or polyester primer prepared in advance, with furniture decoration works.
PB00.812.99 : 100
SP.215 : 100
PLT-4000/SLT-2000 : 10-15
Surface must be clean and dry, free of dirt and dust.
Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 3 layers of 90+110+110 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
12 kg /3 kg
*The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.

PB00.810.99
Polyurethane High-Gloss Black Paint
Polyurethane
1,30± 0,03
75± 5
67± 3
95± 3
25± 5
75± 15
24± 5
3± 1
*Excellent spread and plump appearance after application
*Resistance to yellowing
*Higher hiding power *Fast drying
It is applied as a top coat paint on all kinds of MDF, solid and veneered wooden surfaces, polyurethane or polyester primer prepared in advance, with furniture decoration works.
PB00.810 : 100
SP.170 : 50
PLT-4000/SLT-2000 : 20-25
Surface must be clean and dry, free of dirt and dust.
Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 3 layers of 80-110-110 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
12 kg /3 kg
*The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.

PB00.875
Polyurethane High-Gloss White Paint
Polyurethane
1,22± 0,03
85± 5
65± 3
95± 3
15± 5
40± 5
24± 5
3± 1
*Good spread and plump appearance after application
*Fast drying
It is applied as a top coat paint on all kinds of MDF, solid and veneered wooden surfaces, polyurethane or polyester primer prepared in advance, with furniture decoration works.
PB00.875 : 100
SP.100 : 50
PLT-4000/SLT-2000 : 10-15
Surface must be clean and dry, free of dirt and dust.
Before use, it should be mixed thoroughly and homogenized. Suitable surface after mixing with suitable thinner and hardener
It is applied with a pistol on it. If the temperature is 23°C between the coats, after waiting for 25-30 minutes, 3 layers of 90+110+110 gr/m2 can be cross-applied. During the application, the ambient temperature should not be below 5 °C.
It should be stored in closed packages, in a dry clean, cool environment that will not be exposed to direct sunlight. In its original packaging, the stock period is 1 year.
12 kg /3 kg
*The values are valid at 23°C ambient temperature and 50% ± 10% relative humidity conditions.